Significant improvement of high-temperature oxidation resistance of HfC/SiC ceramic nanocomposites with the incorporation of a small amount of boron

Oxidation behavior of boron-containing HfC/SiC nanocomposites (SHBC) at temperatures up to 1500 °C and with exposure time up to 100 h was investigated. Two strategies to improve the oxidation resistance of the HfC/SiC ceramics are proposed. First concept involves the incorporation of a small amount of boron (ca. 0.6 wt.%) into the nanocomposite via a single-source-precursor approach, which contributes significantly to the enhancement of its oxidation resistance. Parabolic oxidation rate constants of 10⁻³ to 10^-4 mg²/(cm⁴ h) at 1300−1500 °C were measured for SHBC and were several orders of magnitude lower than those recorded for boron-free HfC/SiC. The second improvement concept is realized via passivation of the samples upon short-term oxidation at 1400 °C, providing an excellent oxidation resistance over a wide temperature range. This is a crucial step especially when considering the poor oxidation behavior of HfC and the sluggish formation of protective silica scale at moderate temperatures.     

改良森吉米尔法退火炉中带钢的氧化研究

总结了带钢经过改良森吉米尔退火炉后的4种氧化状态,通过现场实际生产经验的总结和数据积累,分析了带钢产生表面氧化的关键因素,指出了实际操作中应该注意的事项,为以后的设计调试及生产提供了参考。     

高速钢轧辊表面氧化膜研究

借助Gleeble 3500模拟机模拟了高速钢轧辊服役时表面工作层温度的升高,得到了循环加热冷却30次、50次及100次后试样表面的氧化膜。为对比分析,对高铬铸铁轧辊进行了循环50次的试验。利用扫描电子显微镜、X射线衍射分析仪、原子力显微镜对循环氧化后的试样表面氧化产物及其形貌进行了分析。结果表明:随着循环次数增加,高速钢轧辊氧化程度加剧,氧化膜更加致密;同样循环次数下,高铬铸铁轧辊氧化程度要比高速钢严重且氧化膜的粗糙度也大于高速钢。     

Direct synthesis of Fe-ZSM-5 zeolite and its prospects as efficient electrode material in methanol fuel cell

New method of direct synthesis of Fe-ZSM-5 zeolite using tetrapropyl ammonium bromide (TPABr) as the template is reported in this study. The synthesis was based on one step procedure and did not involve the usual ion-exchange step to effect incorporation of the metal ion. The zeolite sample was characterized by XRD, FT-IR, TGA, SEM with EDX, and BET adsorption techniques. The average diameter of the porous particle of zeolite was about 10 µm and it was a spherical cluster of crystals of about 141 nm long along one of its axis. Zeolite-modified glassy carbon electrode (GCE) was prepared by using the mixture of the synthesized zeolite and carbon black (Vulcan X-72) and casting it as a thin layer. With modified GCE as the working electrode, the oxidation of methanol in alkaline medium was studied by cyclic voltammetry. The response of the electrode for methanol oxidation in alkaline medium is promising and it highlights the candidature of the synthesized material for methanol fuel cell. The electrochemical behavior of Fe-ZSM-5 in acidic medium reveals the oxidation state of iron in the zeolite. Cationic iron in the zeolite framework imparts electrocatalytic activity for methanol oxidation.